Name: Shofu Zirconomer Improved - Sri Jeyam Traders
Price: 2750.00 INR
Availability: OutOfStock

Key Specifications

SHADE – U (Universal)
COMPOSITION :

Powder : Fluoroaluminosilicate glass, Zirconium oxide,
pigments and others
Liquid : Polyacrylic acid solution and Tartaric acid

TECHNICAL SPECIFICATIONS :

Powder / Liquid Ratio :	3.6 / 1.0 (2 Scoops : 1 Drop)
Working Time 23˚C :	1 min 30 sec (from start of mixing)
Net Setting Time 37˚C :	3 mins (from end of mixing)

Mechanical Properties	ISO Limit for Amalgam	Zirconomer Improved
Compressive strength @ 1 hour (MPa)	> 80 MPa	149
Compressive strength @ 24 hours (MPa)	> 300 MPa	326
Creep	< 2%	0.01%
Dimensional stability	-0.10% to +0.20%	0.06%

Packaging

1 x 12 gm Powder (Shade : Universal)
1 x 5 ml Liquid
1 x Mixing Pad
1 x Spoon & Spatula

Direction to Use

Preparation: Prepare the tooth for restoration by removing any decay or damaged tooth structure. Clean the tooth and surrounding area thoroughly.
Mixing: Mix the Shofu Zirconomer Improved powder and liquid instructions. The mixing time is typically 10-15 seconds.
Placement: Place the mixed Shofu Zirconomer Improved into the prepared cavity using a suitable instrument. It is important to work quickly as the material will begin to set within a few minutes.
Condensation: Use a suitable instrument to condense the Shofu Zirconomer Improved and ensure it is evenly distributed within the cavity. It is important to avoid overfilling the cavity as this may result in excess material and potential occlusal interferences.
Finishing: Once the material has set, finish and polish the restoration using a suitable polishing system. It is important to avoid over-polishing as this may reduce the material’s strength and wear resistance.

Additional Info

Country of Origin: Japan
Manufacturer: Shofu

Features

High strength and durability like Silver amalgam with protective benefits of glassionomer
Improved edge strength and marginal adaptation
High translucency, flexural modulus and compressive strength
Improved mixing and handling characteristics
Excellent resistance to abrasion and erosion
Remarkable radiopacity
Sustained high fluoride release for anti-cariogenic benefits especially in cases with high caries risk
Exceptional for minimally invasive procedures as it chemically bonds to enamel and dentin while displaying tooth-like co-efficient of thermal expansion, which results in low interfacial stresses and minimizes potential for failure
Packable and condensable like amalgam without the hazard of mercury or the risk of corrosion, expansion and thermal conductivity
For class i & ii, structural base in sandwich restorations, core build-up, root surfaces where overdentures rest, in both pediatric and geriatic cases, as long-term temporary for fractured cusps & fractures amalgam restoratios as well as in ART techniques.

Zirconomer Improved reinforced Glass Ionomer with special zirconia fillers defines a new class of restorative that promises the strength and durability of amalgam with the protective benefits of glass ionomer while completely eliminating the hazards of mercury while proviing sustained fluoride protection. Ideal for a range of restorations including permanent posterior restorative in patients with high risk as well as cases requiring strong structural cores and bases.

Superior Mechanical Properties

Zirconomer Improved outperforms restorative reinforced glass ionomer in stress bearing posterior restorations with notably high compressive strength and dimensional stability for long-lasting performance.

Remarkable Translucency

Zirconomer Improved is formulated with zirconia nano fillers that impart high level of translucency for a closer match to natural tooth colour, ideal even for cores
requiring coverage with high end all-ceramic restoration.

INDICATIONS